Stale odporne na korozję, żaroodporne, żarowytrzymałe, zaworowe i łożyskowe | ||||||
---|---|---|---|---|---|---|
Przeznaczenie | Gatunek w Polskich Normach | Odpowiednik w EN | Odpowiednik w ISO | |||
Gatunek | Norma | Gatunek | Norma | Gatunek | Norma | |
Odporne na korozję | 0H13 | PN-71/H-86020 | X6Cr13 | EN 10088/1-3: 1995 | - | ISO 683-13: 1986 |
0H13J | X6CrA113 | 1 | ||||
H17 | X6Cr17 | 8 | ||||
1H13 | X10Cr13 | - | ||||
3H13 | X30Cr13 | - | ||||
0H17T | X3CrTi17 | - | ||||
H18 | - | - | ||||
H13N4G9 | - | - | ||||
00H18N10 | X2CrNi19-11 | 10 | ||||
0H18N9 | X5CrNi18-10 | 11 | ||||
0H18N10T | X6CrNiTi18-10 | 15 | ||||
0H18NN12Nb | X6CrNiNb18-10 | - | ||||
H18N10MT | X6CrNiMoTi17-12-2 | 21 | ||||
1H18N9 | X12CrNi18-8 | 14 | ||||
1H18N9T | X10CrNitI18-10 | 15 | ||||
1H18N12T | - | 13 | ||||
2H18N9 | X12CrNi18-8 | - | ||||
00H17N14M2 | X2CrNiMo17-2-2 | 19a | ||||
0H17N4G8 | - | A-2, A-3 | ||||
0H17N16M3T | - | 25 | ||||
H17N13M2T | X6CrNiMoTi17-12-2 | 21 | ||||
1H17N4G9 | - | - | ||||
0H22N24M4TCu | - | - | ||||
0H23N28M3TCu | - | - | ||||
Odporne na korozję | X2CrNiN18-7 | PN-EN 10088: 1998 | X2CrNiN18-7 | EN 10088: 1995 | - | ISO 9328T.5:1991 |
X2CrNi18-9 | X2CrNi18-9 | - | ||||
X2CrNi19-11 | X2CrNi19-11 | - | ||||
X2CrNiN18-10 | X2CrNiN18-10 | X2CrNiN1810 | ||||
X5CrNi18-10 | X5CrNi18-10 | X5CrNi1810 | ||||
X8CrNiS18-9 | X8CrNiS18-9 | - | ||||
X6CrNiTi18-10 | X6CrNiTi18-10 | X6CrNiTi1810 | ||||
X6CrNiNb18-10 | X6CrNiNb18-10 | X6CrNiNb1810 | ||||
X4CrNi18-12 | X4CrNi18-12 | X4CrNi1812E | ISO 4954 | |||
X1CrNi25-21 | X1CrNi25-21 | - | ||||
X2CrNiMo17-12-2 | X2CrNiMo17-12-2 | X2CrNiMo1712 | ISO 9328T.5 | |||
X2CrNiMoN17-11-2 | X2CrNiMoN17-11-2 | - | ||||
X5CrNiMo17-12-2 | X5CrNiMo17-12-2 | X5CrNiMo17122E | ISO 4954 | |||
X1CrNiMoN25-22-2 | X1CrNiMoN25-22-2 | - | ||||
X6CrNiMoNb17-12-2 | X6CrNiMoNb17-12-2 | - | ||||
X2CrNiMo17-12-3 | X2CrNiMo17-12-3 | - | ||||
X2CrNiMo17-13-3 | X2CrNiMo17-13-3 | X2CrNiMo17133E | ||||
X3CrNiMo17-13-3 | X3CrNiMo17-13-3 | - | ||||
X2CrNiMo18-14-3 | X2CrNiMo18-14-3 | X2CrNiMo1713 | ISO 9328T.5 | |||
X2CrNiMoN18-12-4 | X2CrNiMoN18-12-4 | - | ||||
X2CrNiMo18-15-4 | X2CrNiMo18-15-4 | X3CrNiMoN18164 | ||||
Odporne na korozję | X2CrNiMoN17-13-5 | PN-EN 10088: 1998 | X2CrNiMoN17-13-5 | EN 10088: 1995 | X2CrNiMoN17135 | ISO 9328T.5 |
X1CrNiSi18-15-4 | X1CrNiSi18-15-4 | - | ||||
X12CrMnNoN17-7-5 | X12CrMnNoN17-7-5 | - | ||||
X2CrMnNiN17-7-5 | X2CrMnNiN17-7-5 | - | ||||
XCrNiCu18-9-2 | XCrNiCu18-9-2 | - | ||||
X6CrNiCuS18-9-2 | X6CrNiCuS18-9-2 | - | ||||
X3CrNiCu18-9-4 | X3CrNiCu18-9-4 | X3CrNiCu1893E | ISO 4954 | |||
X2CrNiN23-4 | X2CrNiN23-4 | - | ||||
X3CrNiMoN27-5-2 | X3CrNiMoN27-5-2 | - | ||||
X2CrNiMoN22-5-3 | X2CrNiMoN22-5-3 | - | ||||
X2CrNiMoN25-7-4 | X2CrNiMoN25-7-4 | - | ||||
X2CrNi12 | X2CrNi12 | - | ||||
X2CrTi12 | X2CrTi12 | ~X6CrTi12E | ||||
X6CrNiTi12 | X6CrNiTi12 | - | ||||
X6Cr13 | - | X6Cr13 | ISO 4955 | |||
X6CrA113 | X6CrA113 | - | ||||
X2CrTi17 | X2CrTi17 | - | ||||
X6Cr17 | - | X6Cr17 | ||||
X3CrTi17 | X3CrTi17 | - | ||||
X3CrNb17 | X3CrNb17 | - | ||||
Odporne na korozję | X6CrMo17-1 | PN-EN 10088: 1998 | X6CrMo17-1 | EN 10088: 1995 | X6CrMo171E | ISO 4954 |
X6CrMoS17 | X6CrMoS17 | - | ||||
X2CrMoTi17-1 | X2CrMoTi17-1 | - | ||||
X2CrMoTi18-2 | X2CrMoTi18-2 | - | ||||
X2CrMoTiS18-2 | X2CrMoTiS18-2 | - | ||||
X6CrNi17-1 | X6CrNi17-1 | - | ||||
X6CrMoNb17-1 | X6CrMoNb17-1 | - | ||||
X2CrNbZr17 | X2CrNbZr17 | - | ||||
X2CrA1Ti18-2 | X2CrA1Ti18-2 | - | ||||
X2CrTiNb18 | X2CrTiNb18 | - | ||||
X2CrMoTi29-4 | X2CrMoTi29-4 | - | ||||
X12Cr13 | - | X12Cr13E | ||||
X12CrS13 | X12CrS13 | - | ||||
X20Cr13 | X20Cr13 | - | ||||
X30Cr13 | X30Cr13 | - | ||||
Odporne na korozję | X29Cr13 | PN-EN 10088: 1998 | X29Cr13 | EN 10088: 1995 | - | ISO 4954 |
X39Cr13 | X39Cr13 | - | ||||
X46Cr13 | X46Cr13 | - | ||||
X50CrMoV15 | X50CrMoV15 | - | ||||
X70CrMo15 | X70CrMo15 | - | ||||
X14CrMoS17 | X14CrMoS17 | - | ||||
X39CrMo17-1 | X39CrMo17-1 | - | ||||
X105CrMo17 | X105CrMo17 | ~110CrMo17 | ISO 4957 | |||
X90CrMoV18 | X90CrMoV18 | - | ||||
X17CrNi16-2 | X17CrNi16-2 | - | ||||
X3CrNiMo13-4 | X3CrNiMo13-4 | - | ||||
X4CrNiMo16-5-1 | X4CrNiMo16-5-1 | - | ||||
X5CrNiCuNb16-4 | X5CrNiCuNb16-4 | - | ||||
X7CrNiA117-1 | X7CrNiA117-1 | - | ||||
X8CrNiMoA115-7-2 | X8CrNiMoA115-7-2 | - | ||||
X10CrNi18-8 | X10CrNi18-8 | X10CrNi189E | ISO 4954 | |||
Żaroodporne | H5M | PN-71/H-86022 | - | EN 10095: 1995 | - | ISO 683-13: 1986 |
H6S2 | - | - | ||||
2H17 | - | - | ||||
H13JS | X10CrA1Si13 | - | ||||
H18JS | X2CrNiMo17-2-2 | EN 10088-1: 1995 | 19a | |||
H24JS | X10CrA1Si25 | - | ||||
H25T | - | - | ||||
H26N4 | - | - | ||||
Żarowytrzymałe | H18N9S | PN-71/H-86022 | - | EN 10095: 1995 | - | ISO 683-13: 1986 |
H23N13 | - | - | ||||
H20N12S2 | X15CrNiSi20-2 | - | ||||
H23NN18 | - | - | ||||
H25N20S2 | X15CrNiSi25-21 | - | ||||
H18N25S2 | - | - | ||||
H16N36S2 | X12NiCrSi35-16 | - | ||||
Zaworowe | H9S2 | PN-71/H-86022 | X45CrSi8 | EN 90: 1971 | - | ISO 683-13: 1986 |
H10S2M | X40CrSiMo10 | - | ||||
4H14N14W2M | - | - | ||||
50H21G9N4 | X53CrMnNiN21-9 | - | ||||
Na łożyska toczne | ŁH15 | PN-74/H-84041 | 100Cr6 | EN 94: 1973 | 1 | ISO 683-17: 1976 |
ŁH15SG | 100CrMn6 | 3 | ||||
LH20M | PN-H-94021: 1997 | - | - |
Legenda:
” – ” oznacza, że w normach europejskich bądź międzynarodowych nie występuje dany gatunek materiału.
” ~ ” oznacza, że gatunek stali występujący w normach europejskich lub międzynarodowych różni się składem chemicznym od gatunku materiału występującego w normach europejskich.